Title: REAÇÃO ÁLCALI-AGREGADO PELO MÉTODO ACELERADO EM PRISMAS DE CONCRETO: avaliação de agregados de quartzito provenientes do município de São Thomé das Letras-MG
Other Titles: GABRIEL DE ABREU MENEZES
metadata.dc.creator: Menezes, Gabriel de Abreu
metadata.dc.contributor.advisor1: Júnior, Ivan Francklin
metadata.dc.description.resumo: A engenharia está em constante evolução, permitindo-se estudar problemas que antes não eram possíveis por falta de tecnologia. O material mais utilizado na construção civil é o concreto e existem várias patologias que afetam a sua durabilidade e resistência mecânica. Uma dessas patologias é conhecida com reação álcali-agregado (RAA), trata-se de uma reação química que ocorre no interior do concreto já endurecido, entre componentes do cimento e do agregado quando a estrutura se encontra em contato com água. A RAA produz um gel que se expande e gera tensões de tração no interior do concreto causando fissurações que diminuem a sua resistência mecânica. Foi realizado um estudo de potencialidade reativa em concretos produzidos com o agregado graúdo de quartzito proveniente de estéril de extração da cidade de São Thomé das Letras, sul de Minas Gerais. O estudo foi embasado na norma ABNT NBR 15577:2018, que determina todos os parâmetros e requisitos para a realização dos ensaios de verificação de RAA. O estudo contempla as seguintes etapas: definição dos materiais para a produção do concreto; determinação dos índices físicos dos materiais; produção dos concretos e realização das medições. Nesta etapa foi realizada uma análise petrográfica para verificar a composição mineralógica do quartzito e também a produção dos prismas de concreto pelo método acelerado onde a duração do ensaio é de 20 semanas para constatar a potencialidade reativa. No conteúdo do trabalho são apresentados os resultados da análise petrográfica realizada na Universidade Estadual Paulista (UNESP) – Campus de Rio Claro e medidas de variação de expansão dos prismas de concreto. O resultado da análise foi satisfatório devido à inicial classificação reativa do agregado, entretanto em relação aos prismas ainda não foram finalizados os ensaios, mas já se pode afirmar que o agregado atingiu um grau de potencialidade reatividade como foi previsto na análise petrográfica.
Abstract: Engineering is in constant evolution, allowing us to study problems that were not possible before due to lack of technology. The most used material in civil construction is concrete and there are several pathologies that affect its durability and mechanical resistance. One of these pathologies is known as alkali-aggregate reaction (AAR); it is a chemical reaction that occurs inside the already hardened concrete, between cement and aggregate components when the structure is in contact with water. The AAR produces a gel that expands and generates tensile stresses inside the concrete causing cracks that reduce its mechanical strength. A study of reactive potentiality in concrete produced with the coarse quartzite aggregate from extraction tailings from the city of São Thomé das Letras, southern Minas Gerais, was performed. The study was based on the ABNT NBR 15577:2018 standard, which determines all parameters and requirements for the performance of AAR verification tests. The study contemplates the following steps: definition of materials for the production of concrete; determination of the physical indexes of materials; production of concrete and performance of measurements. In this step, a petrographic analysis was performed to verify the mineralogical composition of the quartzite and also the production of the concrete prisms by the accelerated method where the test duration is 20 weeks to verify the reactive potentiality. The results of the petrographic analysis carried out at Universidade Estadual Paulista (UNESP) - Rio Claro Campus and measures of the variation of the expansion of the concrete prisms are presented in the study content. The result of the analysis was satisfactory due to the initial reactive classification of the aggregate, however in relation to the prisms the tests have not yet been finalized, but it can already be stated that the aggregate reached a degree of reactivity potentiality as predicted in the petrographic analysis
Keywords: Reação álcali-agregado
potencialidade reativa
análise petrográfica
metadata.dc.subject.cnpq: Engenharias
metadata.dc.language: por
metadata.dc.publisher.country: Brasil
Publisher: Fundação de Ensino e Pesquisa do Sul de Minas
metadata.dc.publisher.initials: FEPESMIG
metadata.dc.publisher.department: Centro Universitário
metadata.dc.rights: Acesso Aberto
URI: http://repositorio.unis.edu.br/handle/prefix/2523
Issue Date: 6-Dec-2019
Appears in Collections:Engenharia Civil
Engenharia Civil

Files in This Item:
File Description SizeFormat 
TCC Gabriel Menezes.pdf2,24 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.